Master Bond EP41SMed Two Component, Low Viscosity, USP Class VI Epoxy System

Master Bond Polymer Adhesive EP41S Medical is a two component low viscosity epoxy resin system for high performance bonding, sealing, coating, as well as small encapsulations, pottings and castings. It is formulated to cure readily at room temperature or more quickly at elevated temperatures. One notable property is its very fast curing at room temperature. EP41S Medical meets USP Class VI specifications, making it well suited for a variety of uses in medical devices as an adhesive, sealant and coating.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
粘度	cP	cP	Part B
	cP	cP	mixed compound
	cP	cP	Part A

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度	>= MPa	>= psi
拉伸模量	GPa	ksi
粘合强度	>= MPa	>= psi	after 30 days water absorption
	>= MPa	>= psi

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	>= ohm-cm	>= ohm-cm
介电强度	>= kV/mm @Thickness 3.17 mm	>= kV/in @Thickness 0.125 in

热性能	额定值 (公制)	额定值 (英制)	测试方法
最高工作温度, Air	°C	°F
最低工作温度, Air	°C	°F

加工性能	额定值 (公制)	额定值 (英制)	测试方法
固化时间	min @Temperature 100 °C	hour @Temperature 212 °F
	min @Temperature 23.9 °C	hour @Temperature 75.0 °F
适用期	min	min	100 gram mass
保质期	Month	Month	in unopened containers

材料描述		测试方法
Mixing Ratio (A to B)	5/1