Kalix® 9950物性表-搜物性

Kalix® 9950 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties and excellent surface quality.

Kalix® 9950 is characterized by high stiffness and strength, very good impact properties, good dimensional stability, low warpage behavior and excellent surface finish. It can be successfully plated, for example with non conductive vacuum metallization, or painted with soft touch or UV top coat paints. Please contact your Solvay Specialty Polymers sales representative for more information on suitable plating and painting systems.

Kalix® 9950 exhibits an excellent combination of high flow, low flash tendency and fast cycle time which makes it a cost-competitive option for thin-walled parts produced in large quantities, such as structural parts in mobile electronic devices.

Black: Kalix® 9950 BK 000

White: Kalix® 9950 WH 000

Natural: Kalix® 9950 NT 000

基本信息
黄卡编号	E95746-101004610
填料/增强材料	玻璃纤维增强材料, 50% 填料按重量
特性	尺寸稳定性良好低翘曲性刚性，高高强度抗撞击性，良好可电镀可喷涂的快的成型周期流动性高热水可成型性优良外观
用途	薄壁部件电气/电子应用领域电气元件手机
RoHS 合规性	RoHS 合规
外观	白色黑色可用颜色自然色
形式	粒子
加工方法	水温模具注塑成型注射成型
部件标识代码 (ISO 11469)	>PAMXD6/66-GF50

物理性能	单位制	测试方法
比重	g/cm³	ASTM D792
收缩率 ¹		内部方法
垂直流动方向	%	内部方法
流动方向	%	内部方法
吸水率 (23°C, 24 hr)	%	ISO 62

机械性能	单位制	测试方法
拉伸模量	MPa	ISO 527-2
拉伸应力 (屈服)	MPa	ISO 527-2
拉伸应变 (断裂)	%	ISO 527-2
弯曲模量	MPa	ISO 178
弯曲应力 (3.5% 应变)	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度		kJ/m²	ISO 180/1A
无缺口伊佐德冲击强度		kJ/m²	ISO 180

热性能	单位制	测试方法
热变形温度
0.45 MPa, 未退火	°C	ISO 75-2/B
1.8 MPa, 未退火	°C	ISO 75-2/A
熔融温度	°C	ASTM D3418

电气性能	额定值		测试方法
介电常数 ²			ASTM D2520
1.00 GHz			ASTM D2520
2.40 GHz			ASTM D2520
耗散因数 ³			ASTM D2520
1.00 GHz			ASTM D2520
2.40 GHz			ASTM D2520

可燃性	额定值		测试方法
UL 阻燃等级 (0.600 mm, 所有颜色)			UL 94

补充信息
Typical values shown tested on Dry as Molded samples.Standard Packaging and Labeling: Kalix 9950 resin is packaged in foil lined, multiwall paper bags containing 25 kg (55 pounds) of material. Individual packages will be plainly marked with the product number, the color, the lot number, and the net weight.

注射	额定值	单位制
干燥温度		°C
干燥时间		hr
料筒后部温度		°C
料筒前部温度		°C
加工（熔体）温度		°C
模具温度		°C

注射说明
Storage: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Kalix® processing guide. Drying: Kalix 9950 is supplied in sealed bags. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Kalix 9950 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 285°C and 305°C (545°F and 580°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 280°C (536°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled.

注射说明

Storage: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Kalix® processing guide. Drying: Kalix 9950 is supplied in sealed bags. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Kalix 9950 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 285°C and 305°C (545°F and 580°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 280°C (536°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled.

备注
1 .	索尔维测试方法。收缩率会根据部件的设计和加工条件而改变。请接洽索尔维技术代表，获取更多信息。
2 .	方法 B
3 .	方法 B

Kalix® 9950

HPPA

Solvay Specialty Polymers

产品说明